Neodymium Countersunk Magnet

Descriptio:

Neodymium magnetum calculi sunt genus muneris magnetum permanentium. Magnetes calculi foramen habent, ergo facile est in superficiem figere cochleae matching utendo. Quia ex vi magnetica, neodymium magnetum calculis praefertur electio multorum applicationum edax, mercatorum et technicorum.

Zhongke propria est in fabricandis et providendis magnetibus cylindricis neodymium adhibitis in variis applicationibus industriae cum technicis provectis, experientia dives, et technicis professionalibus technicis.

+86-15857968349 mahy@dymagnet.com

A Quote

Magnitudo chart
Morbi laoreet euismod
Superficies Coating
Magnetization Directio

Product Name	Magnitudo Type	Machinabiles dimensiones (secundum magnitudinem distingui possunt), cum tolerantiae
Neodymium Countersunk Magnet	L/W	1、0.2mm
		3、20.0mm
		3、20.0mm
	H	1、0.2mm
		2、3.00mm
		3、H>10.0mm，Tolerances±0.05mm
	idipsum	1、L×W≤25.0mm²，Flatness±0.02mm
		2、25.0mm²
		3、400.0mm²
	Parallelismus	1、0.20mm
		2、5.00mm
		3、30.0mm
		4、L/W>75.0mm，Parallelism±0.10mm
	C Anglus	C≥0.1mm







	R Anglus	R≥0.1mm

Characteres De Sintered NdFeB Magnet Sub 23 ℃ /-2 ℃
Euismod	Remanence Inductio Intensionem (Br)		Magna vis coactiva (Hcb)		Intrinsic Coercivity (Hcj)		Maximum Energy Product (BH)max		Quadratum factores (Hk/Hcj)	Maximum Opus Temperature Tw L/D = 0.7
Gradus	Min		Min		Min		Range		Min	Maximum Opus Temperature Tw L/D = 0.7
Gradus	T	kGs	KA/m	kOe	KA/m	kOe	kA/m³	MGOe	%	°c
N28ZH	1.04	10.4	772	9.7	3184	40	207~239	26~30	90	250
N44AH	1.30	13.0	971	12.2	2786	35	326~358	41~45	90	230
N42AH	1.29	12.9	963	12.1	2786	35	318~ 350	40~44	90	230
N40AH	1.26	12.6	939	11.8	2786	35	302~ 334	38~42	90	230
N35AH	1.17	11.7	868	10.9	2786	35	263~ 295	33~37	90	230
N30AH	1.08	10.8	804	10.1	2786	35	223~255	28~32	90	230
N42TH	1.29	12.9	957	11.8	2627	33	318 ~ 342	43 ~ 46	90	220
N40TH	1.26	12.6	930	11.5	2627	33	302 ~ 326	40 ~~ 43	90	220
N38TH	1.23	12.3	910	11.1	2627	33	287 ~~310	38 ~ 41	90	220
N35TH	1.18	11.8	876	11	2786	35	263 ~ 287	36 ~ 39	90	220
N33TH	1.13	11.3	844	10.6	2786	35	247 ~ 270	33 ~ 36	90	220
N30TH	1.1	11	796	10	2786	35	223 ~247	31 ~ 33	90	220
N28TH	1.05	10.5	756	9.5	2786	35	207 ~ 230	25 ~ 29	90	220
N45EH	1.33	13.3	995	12.5	2308	29	342 ~ 366	45 ~ 49	90	200
N42EH	1.29	12.9	957	11.8	2308	29	318 ~ 342	43 ~ 46	90	200
N40EH	1.26	12.6	930	11.5	2388	30	302 ~ 326	40 ~~ 43	90	200
N38EH	1.23	12.3	910	11.1	2388	30	287 ~~310	38 ~ 41	90	200
N35EH	1.18	11.8	876	11	2388	30	263 ~ 287	36 ~ 39	90	200
N33EH	1.13	11.3	844	10.6	2388	30	247 ~ 270	33 ~ 36	90	200
N30EH	1.1	11	796	10	2388	30	223 ~247	31 ~ 33	90	200
N28EH	1.05	10.5	756	9.5	2388	30	207 ~ 230	25 ~ 29	90	200
N52UH	1.42	14.2	1018	12.8	1911	24	390 ~ 422	49 ~~ 53	90	180
N50UH	1.39	13.9	1018	12.8	1911	24	374 ~~ 406	47 ~ 51	90	180
N48UH	1.37	13.7	1018	12.8	1911	24	358 ~ 390	45 ~ 49	90	180
N45UH	1.33	13.3	995	12.5	1911	24	342 ~ 366	45 ~ 49	90	180
N42UH	1.29	12.9	957	11.8	1990	25	318 ~ 342	43 ~ 46	90	180
N40UH	1.26	12.6	930	11.5	1990	25	302 ~ 326	40 ~~ 43	90	180
N38UH	1.23	12.3	910	11.1	1990	25	287 ~~310	38 ~ 41	90	180
N35UH	1.18	11.8	876	11	1990	25	263 ~ 287	36 ~ 39	90	180
N33UH	1.13	11.3	844	10.6	1990	25	247 ~ 270	33 ~ 36	90	180
N30UH	1.1	11	796	10	1990	25	223 ~247	31 ~ 33	90	180
N28UH	1.05	10.5	756	9.5	1990	25	207 ~ 230	28 ~ 31	90	180
N52SH	1.42	14.2	1018	12.8	1512	19	390 ~ 422	49 ~~ 53	90	150
N50SH	1.39	13.9	1018	12.8	1512	19	374 ~~ 406	47 ~ 51	90	150
N48SH	1.37	13.7	1018	12.8	1512	19	358 ~ 390	45 ~ 49	90	150
N45SH	1.33	13.3	995	12.5	1592	20	342 ~ 366	45 ~ 49	90	150
N42SH	1.29	12.9	957	11.8	1592	20	318 ~ 342	43 ~ 46	90	150
N40SH	1.26	12.6	930	11.5	1592	20	302 ~ 326	40 ~~ 43	90	150
N38SH	1.23	12.3	910	11.1	1592	20	287 ~~310	38 ~ 41	90	150
N35SH	1.18	11.8	876	11	1592	20	263 ~ 287	36 ~ 39	90	150
N33SH	1.13	11.3	844	10.6	1592	20	247 ~ 270	33 ~ 36	90	150
N30SH	1.1	11	796	10	1592	20	223 ~247	31 ~ 33	90	150
N28SH	1.05	10.5	756	9.5	1592	20	207 ~ 230	28 ~ 31	95	150
N55H	1.45	14.5	1035	13	1274	16	406 ~~ 438	53 ~~ 56	95	120
N52H	1.42	14.2	1035	13	1274	16	390 ~ 422	49 ~~ 53	95	120
N50H	1.39	13.9	1035	13	1274	16	374 ~~ 406	47 ~ 51	95	120
N48H	1.37	13.7	1018	12.8	1274	16	358 ~ 390	45 ~ 49	95	120
N45H	1.33	13.3	995	12.5	1353	17	342 ~ 366	45 ~ 49	95	120
N42H	1.29	12.9	957	12	1353	17	318 ~ 342	43 ~ 46	95	120
N40H	1.26	12.6	930	117	1353	17	302 ~ 326	40 ~~ 43	95	120
N38H	1.23	12.3	910	11.4	1353	17	287 ~~310	38 ~ 41	95	120
N35H	1.18	11.8	876	11	1353	17	263 ~ 287	36 ~ 39	95	120
N33H	1.13	11.3	844	10.6	1353	17	247 ~ 270	33 ~ 36	95	120
N30H	1.1	11	796	10	1353	17	223 ~247	31 ~ 33	95	120
N28H	1.05	10.5	756	9.5	1353	17	207 ~ 230	28 ~ 31	95	120
N55M	1.45	14.5	995	12.5	1035	13	406 ~~ 438	51 ~~ 55	95	100
N52M	1.42	14.2	995	12.5	1035	13	390 ~ 422	49 ~~ 53	95	100
N50M	1.39	13.9	1035	13	1114	14	374 ~~ 406	47 ~ 51	95	100
N48M	1.37	13.7	1012	12.7	1114	14	358 ~ 390	45 ~ 49	95	100
N45M	1.33	13.3	971	12.2	1114	14	342 ~ 366	43 ~ 46	95	100
N42M	1.29	12.9	938	11.8	1114	14	318 ~ 342	40 ~~ 43	95	100
N40M	1.26	12.6	910	11.4	1114	14	302 ~ 326	38 ~ 41	95	100
N38M	1.23	12.3	876	11	1114	14	287 ~~310	36 ~ 39	95	100
N35M	1.18	11.8	860	10.8	1114	14	263 ~ 287	33 ~ 36	95	100
N33M	1.13	11.3	796	10	1114	14	247 ~ 270	31 ~ 33	95	100
N30M	1.1	11	796	10	1114	14	223 ~247	28 ~ 31	95	100
N28M	1.05	10.5	756	9.5	1114	14	207 ~ 230	26 ~ 29	95	100
N55	1.45	14.5	836	10.5	875	11	406 ~~ 438	51 ~~ 55	95	80
N54	1.45	14.5	836	10.5	876	11	406 ~ 438	51 ~ 55	95	80
N52	1.42	14.2	860	10.8	960	12	390 ~ 422	49 ~~ 53	95	80
N50	1.39	13.9	860	10.8	960	12	374 ~~ 406	47 ~ 51	95	80
N48	1.37	13.7	860	10.8	960	12	358 ~ 390	45 ~ 49	95	80
N45	1.33	13.3	836	10.5	960	12	342 ~ 366	43 ~ 46	95	80
N42	1.29	12.9	836	10.5	960	12	318 ~ 342	40 ~~ 43	95	80
N40	1.26	12.6	836	10.5	960	12	302 ~ 326	38 ~ 41	95	80
N38	1.23	12.3	836	10.5	960	12	287 ~~310	36 ~ 39	95	80
N35	1.18	11.8	836	10.5	960	12	263 ~ 287	33 ~ 36	95	80
N33	1.13	11.3	796	10	960	12	247 ~ 270	31 ~ 34	95	80

Genus coating		Crassitudo	Exterior	Corrosio Resistentia					Animadverte
Genus coating		Crassitudo	Exterior	PCT	Sal Spray	Umor et Temperature	Acidum/Alkali	Oleum	Animadverte
Zn (White Zn)	√	≥5μm	Hyacinthum album	--	★★	★★★	--	★
Zn (Color-patella Zn)	√	≥5μm	Iridescent	--	★★★	★★★★	--	★
Ni Cu Ni	√	≥15μm	Argentea alba	★★★	★★★★	★★★★★	★★★	★★★
Ni Cu Ni Sn		≥15μm	Argentea alba	★★★★	★★★★	★★★★★	--	--	Optimum Eelding euismod
Chemic Ni	√	≥5μm	Argentea alba	★★★★	★★★★★	★★★★★	★★★	★★★
Epoxy	√	≥12μm	Nigrum vel Grey	★★★	★★★★★	★★★★★	★★★★★	★★★★	Pauperes gere Resistentia
passivated	√	≤2μm	Nigrum vel Grey	--	--	★★★	--	★★★
Al		≥3μm	Argentum Grey	★★★★	★★★	★★★★	--	★★★	High binding Force
Al Epoxy		≥15μm	Nigrum vel Grey	★★★★★	★★★★★	★★★★★	★★★★★	★★★★★	Pauperes gere Resistentia
Zn Al		≥10μm	Argentum album aut argentum Grey	★★★★★	★★★★★	★★★★★	--	★★★★★
Everluber		≥5μm	Aureum	★★★★	★★★★	★★★★★	★★★★★	★★★★
Teflon		≥5μm	nigreos	★★	★★★	★★★★★	★★★★★	★★★	Bene gere Resistentia


Disc Axial	Disc Diametrica	Cylindrus Axial	Cylindrus Diametricus

Annulus Axial	Anulum Diametricum	Annulus Cylindrus Axial	Annulus Cylindrus Diametrical

Obstructionum-Rectangle Crassitudo	Obstructionum-Rectangle Longitudo

Arcus Latitudo	Arcus Altitudo	Arcus Diametricus	Arcus Diametrical

Related Products

Sintered NdFeB Materiae magneticae permanentes

Zhejiang Zhongke magnes lndustry Co., Ltd. est opifex professionalis magnetis ferriti et neodymii magnetis per multos annos. lts producta summus qualitas includunt magnetem sinteredum neodymium permanentem et magnetem ferritum sinteratum, qui late in electronicis consumptis, industria salutaris adjumenta alba, nova vehiculi industria, etc. Plus quam 4000 possidet, maxime praebetur magnis et medialibus clientibus. domi forisque, inter SAMSUNG, Amazon, Nidec, Xiaomi, GREE, Midea, WOLONG, etc.

Rudis Material Ratio

Materias solidas rudis ut praseodymium et neodymium metallorum, ferrum purum et ferroboron in proportione commisce.
Smelting

Mixtae materiae rudis per fornacem excoquunt, et inde vivos bracteas bracteae tenues stannum formatur expoliatione.
Contritio pulveris

Rapienti bracteae bracteae tenuissimae in mixturae mixturae pulvere per secundae fornacis comminuendae contusae sunt, et deinde pulvis offensionis tenuis in mixturae pulveris milling.
Press CUMATIUM

Pulvis sub tutela nitrogenii in pactum deprimendo factus est.
Vacuum Sinter

Pactum calefit ad caliditatem caliditatis in fornace sintering in ambitu vacuo et postea curationi calori senescente subiecta est ut formaret NdFeB blank.
Mechanica Processing

Utere instrumento professionali ad processum blank secundum exigentias specificas ordinis pro figura et magnitudine, inclusa stridor, filum secans, dividens, pulsans, etc.
Diffusio frumenti circumscriptio

Magnetis superficiem cum metallo terreno gravi rariori vel composito operire, et elementum terrae graue rarioris in intus sinteratum magnetis NdFeB calefacere diffundi.
Superficiem treatment

Ut ad requisita perficienda resistentiae et corrosionis induendi resistentia, stridor mechanica et curatio electrochemica in magnete superficie feruntur.
Magnetizing

Secundum necessitates ordinis, magneticam magnetem in agro magnetico utendo.
Inspectionis et Packaging

Secundum exigentias ordinis, proprietates magneticae, species, magnitudo, corrosio resistentia et aliae proprietates magnetum inspiciuntur, et fasciculus et repositio nonnisi post inspectionem peractam peragi possunt.

< >

Productio Commoda

Processus Milling

Societas technologias applicat ut technologiae cristallinae columnar proiectionis incrementum technologiam, frumenti elegantiam et technologiam micro-optimizationem, etc., et committatur ad solidam pulveris meliorandam et plenam praebendam lusum ad potentiam rarae terrae perficiendam. Improvendo microstructuram excoquunt, technologiam frumenti technologiam applicando, et processum miscentem optimizing, etc., signanter emendans magnetum NdFeB observantiam.
Formans et Sintering Processus

Societas magnes ad praeparationem technologiam et frigus isostaticum prementem technologiam low-oxygeni adhibuit et emendavit, ita ut magnetes NdFeB in statu humili oxygeni durante processu presso sint, et praeparatio blanksicae continenter optimized, quae efficaciter minuit iacturam. rara terra. Applicatio technicae artis humilis temperaturae caloris sintering ulterius processum sintering emendavit. Temperantiae apto statui adaptans plenam ludere peractae formulae potest. Repraesentativae producta sunt altae operationes magnetes N55 paratae ab technologia low-oxygen et magnetes N38UH producti per technologiam fabricam prope rete.
Processus Technologiae

Ut accuratam praecisionem institutionis mos persequatur, societas summus perficientur ultra tenues parvas speciales formatas magnetis permanentis praeparationis technologiae ad altam efficientiam et humilem iacturam praecisionis machinæ NdFeB electronicarum perrumpens, perruptionem technicae bottleneck summus effectus tenuis et parvae magnetis difficultas processus, et stricte moderari productum species defectus per aspectum imaginis intelligentis technologiae latae inspectionis ad meliorem inspectionem efficientiam et diligentiam.